Effects of surface defect on thermal stability and stress crack resistance of high density polyethylene geomembranes in environmental conditions were examined by comparing the mechanical properties, chemical resistance and failure times of geomembranes between defective cases under different temperatures. Artificial surface defects were added to the surface of geomembranes by scratch apparatus designed specially. The number of surface defects was increased with the smaller size of scratch induced particles, and the more scratch addition numbers at the shear rate of scratch induced mechanism, 100mm/min. The tensile strength were decreased but the tensile strain was increased with the above conditions. In chemical resistance of defective geomembranes, the tensile strength were decreased but the tensile strain was increased with the longer immersion period and the higher temperature under the same scratch induced conditions. Finally, failure times of defective geomembranes by ESCR test were shifted to the shorter time ranges by increasing temperatures.

표면결함이 고밀도 폴리에틸렌 지오멤브레인의 열적 안정성과 응력균열저항성에 미치는 영향을 온도와 표면 결함 부여조건을 달리한 환경조건에서 역학적 특성, 화학저항성 및 피로시간을 측정하여, 조사하였다. 특별 고안된 장치를 사용하여 인위적으로 지오멤브레인 표면에 결함을 부여하였다. 표면결함은 표면결함 유도매체의 전단속도 100mm/min에서 표면결함 유도매체의 크기가 작을수록, 표면결함 부여횟수가 커질수록 증가하였다. 또한 이 조건에서 인장강도는 감소하였지만 인장신도는 증가하였다. 표면결함 부여조건이 같을 경우 고온으로 갈수록 그리고 침지시간이 길어질수록 인장강도는 감소되고 인장신도는 증가하여 표면결함이 부여된 지오멤브레인의 화학저항성은 저하되었다. 끝으로 응력균열저항성 시험 결과 온도가 높아질수록 표면결함이 부여된 지오멤브레인의 피로시간은 단시간 영역으로 이동되었다.

Keywords: